A woodceramics is prepared from liquefied corncob and poplar powder. The basic property of this material is closely correlated to the carbonization temperature and liquefied corncob content. The thermogravimetric analysis indicates that the high liquefied corncob content can decrease weight loss. X-ray diffraction analysis shows that higher carbonization temperature can improve the graphitization degree of this material, but the phase composition is not mainly related to the liquified corncob content. Scanning electron microscopy confirms that the poplar powder is as a natural plant template and the pore of woodceramics partly keeps the native characteristics of the wood with size ranging from 5 to 20 mu m. It is porous carbon material with three-dimensional network structure.
作者机构：
[王荣; 孙德林] College of Furniture and Art Design, Central South University of Forestry and Technology, Changsha 410004, China;[黄小西] Biotechnology Core Facilities, Central South University of Forestry and Technology, Changsha 410004, China;[孙德彬] College of Material and Engineering, Central South University of Forestry and Technology, Changsha 410004, China;[余先纯] Basis Department, Yueyang Vocational and Technical College, Yueyang 414000, China
通讯机构：
[Sun, D.-L.] C;College of Furniture and Art Design, , Changsha 410004, China