采用不同方法[包括EP（环氧树脂）的pH值调节法、EP中添加改性剂法和改性剂吸附包覆纳米TiO2法等]对纳米TiO2在EP中的分散性进行了研究。结果表明：上述改性方法均能促进纳米TiO2在EP中良好分散：当EP的pH值为3时,相应胶粘剂的剪切强度比pH值未调节体系提高了11.46%;采用EP中添加改性剂法,并且当改性剂为SDBS（十二烷基苯磺酸钠）时,相应胶粘剂的剪切强度比无改性剂体系提高了6.7%;采用改性剂吸附包覆纳米TiO2法,并且当改性剂为SDS（十二烷基磺酸钠）、KH-560（硅烷偶联剂）和SDBS时,相应胶粘剂的剪切强度比无改性剂体系分别提高了41.7%（SDS）、16.4%（KH-560）和9.4%（SDBS）。

The dispersibility of nano-TiO2 in epoxy resin（EP） was investigated by different methods（including adjusting pH value of EP,adding modifier into EP and nano-TiO2 adsorbed-coated by modifier）.The results showed that the aforementioned modified methods can all promote good dispersion of nano-TiO2 in EP.The shear strength of adhesive with EP＇s pH value at 3 was 11.46% more than that of adhesive without adjusted EP＇s pH value.The shear strength of adhesive with sodium dodecyl benzene sulfonate（SDBS） modifier was 6.7% more than that of adhes...