核聚变面对等离子体材料表面损伤、失效是其服役寿命的主要影响因素,利用喷丸技术增强钨面对等离子体材料表面性能。以纯钨为被喷丸强化材料,选择0.5 mm不锈钢丸料,在0.4 MPa喷丸压力、100 mm喷丸距离的喷丸参数下,...展开更多 核聚变面对等离子体材料表面损伤、失效是其服役寿命的主要影响因素,利用喷丸技术增强钨面对等离子体材料表面性能。以纯钨为被喷丸强化材料,选择0.5 mm不锈钢丸料,在0.4 MPa喷丸压力、100 mm喷丸距离的喷丸参数下,研究不同喷丸时间(30,60,120,240 s)对钨材料表面增强效果,主要包括微观组织形貌和粗糙度、表面硬度及其分布、表面残余应力等。结果显示喷丸对钨表面造成损...

The main influence factors on the service life of plasma facing materials for fusion device are the surface damage and failure.Shot peening technology is used to strengthen the surface performances of tungsten plasma facing materials.The shot peening parameters were as ...MORE The main influence factors on the service life of plasma facing materials for fusion device are the surface damage and failure.Shot peening technology is used to strengthen the surface performances of tungsten plasma facing materials.The shot peening parameters were as fo...